Dissolution of Synroc in deionised water at 150°C

Abstract

Synroc containing 20 wt% simulated high level waste (HLW) was subjected to two sets of leach tests at 150°C where the leachant was and was not replaced during the test (replacement and non-replacement testing). The leachant was a KH-phthalate buffered solution (pH 4.2). Samples were characterised before and after leach testing using SEM, AEM and SIMS. Elemental concentrations in leachates were measured using ICP-MS. In concert with the findings of i) a dissolution study of perovskite in a flowing leachant and ii) a previous Synroc dissolution study (wherein Synroc containing 10 wt% simulated HLW was subjected to periodic replacement, leach testing in deionised water at 150°C), the results of this study show that when the leachant replacement frequency is varied from 7 d to the duration of the test, there is no effect on leach rate or leaching mechanisms. © Materials Research Society 1997