Title: Magnetic properties and magnetocaloric effect of NdMn2-xTixSi2 compounds
Authors: Din, MFM
Wang, JL
Campbell, SJ
Zeng, R
Hutchison, WD
Avdeev, M
Kennedy, SJ
Dou, SX
Keywords: Neutrons
Neutron diffraction
Issue Date: 16-Oct-2013
Publisher: IOP Publishing Ltd
Citation: Md Din, M. F. , Wang, J. L., Campbell, S. J., Zeng, R., Hutchison, W. D., Avdeev, M., Kennedy, S. J., & Dou, S. X. (2013). Magnetic properties and magnetocaloric effect of NdMn2-xTixSi2 compounds. Journal of Physics D-Applied Physics, 46(44), Article Number 445002. doi:10.1088/0022-3727/46/44/445002
Abstract: The structural and magnetic properties of the intermetallic compounds NdMn 2− x Ti x Si 2 ( x = 0, 0.1, 0.2, and 0.3) have been studied by x-ray and high resolution neutron powder diffraction, specific heat, dc magnetization, and differential scanning calorimetry measurements over the temperature range 3–450 K. The Curie temperature and Néel temperature of NdMn 2 Si 2 decrease from T C = 36 K and T N = 380 K to T C = 14 K and T N = 360 K, respectively, on substitution of Ti ( x = 0.3) for Mn. The magnetocaloric effect at the first order ferromagnetic phase transition at T C , has been investigated in detail. Under a change of magnetic field of 0–5 T, the maximum value of the magnetic entropy change is 27 J kg −1 K −1 at x = 0, reducing to 15.3 J kg −1 K −1 at x = 0.1 and 10 J kg −1 K −1 at x = 0.3; importantly, no thermal or field hysteresis losses occur (eliminated from 0.3 K and 28.5 J kg −1 at x = 0 around T C ) with increase in Ti concentration. Combined with the lack of any hysteresis effects, these findings indicate that NdMn 1.9 Ti 0.1 Si 2 compound offers potential as a candidate for magnetic refrigerator applications in the temperature region below 35 K. © 2013, IOP Publishing LTD.
Gov't Doc #: 5414
ISSN: 0022-3727
Appears in Collections:Journal Articles

Files in This Item:
There are no files associated with this item.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.